International Journal of Advanced Applied Physics Research  (Volume 1 Issue 1)
 PbZrO3-Based Antiferroelectric Thin Film Capacitors with High Energy Storage Density International Journal of Advanced Applied Physics Research
Pages 35-39

Mao Ye, Peng Lin, Haitao Huang, Biaolin Peng, Qiu Sun, Fuping Wang, Xiang Peng, Xierong Zeng, and Shanming Ke

DOI: http://dx.doi.org/10.15379/2408-977X.2014.01.01.4
Published: 28 August 2014
Abstract
 A series of 400-nm-thick sandwich structured Pb(1+x)ZrO3/(Pb,Eu)ZrO3/Pb(1+x)ZrO3(PZO/PEZO/PZO) antiferroelectric thin films with different Pb excess content (x) (x=0%, 10%, 20%, and 30%) in the PZO precursors have been successfully deposited on Pt(111)/Ti/SiO2/Si substrates by a sol–gel method. The effects of Pb excess content on the dielectric properties, and energy storage performance of the PZO/PEZO/PZO thin films have been investigated in detail. It is found that all the films show a unique perovskite phase structure. With increasing Pb excess content in the PZO precursors, P-E hysteresis loop changes from slanted to square shape. Meanwhile, a larger antiferroelectric to ferroelectric switching field (EAF) and ferroelectric to antiferroelectric switching field (EFA) are observed in the films with higher Pb excess content. When increasing Pb excess content from 0% to 30%, the energy storage density of the sandwich structured films is remarkably improved from 11.4 to 14.8 J/cm3 at 1000 kV/cm.
Keywords
 Electron-phonon interaction, Magnetic excitations, Van Hove singularity, Gap energy, Pseudogap, Coherence length, Isotope coefficient, Superconducting gap ratio.
CTDL

Testimonials

The entire editorial process of Cosmos Scholars Publishing House is ve
Dr. Chandra Mohan
We are very grateful to the editorial body, the entire process was fas
Dr. Yaneth Aguilar Díaz
SiteLock